Abstract
Polymer-textile liner composites have potential applications in aerospace applications for reducing the abrasion damage of moving parts during operation owing to their self-lubrication, light weight, and high loading capacity. Herein, Au nanoparticles (AuNPs) are successfully loaded into the lumen of halloysite nanotubes (HNTs) to construct an HNTs-Au peasecod core-shell nanosystem to optimize the wear resistance of phenolic resin-based poly(p-phenylene benzobisoxazole) (PBO)/polytetrafluoroethylene (PTFE) textile composites. Transmission electron microscope (TEM) characterization reveals that the AuNPs are well-dispersed inside the HNTs, with an average diameter of 6-9 nm. The anti-wear performance of the HNTs and Au-reinforced PBO/PTFE composites is evaluated using a pin-on-disk friction tester at 100 MPa. Evidently, the addition of HNTs-Au induces a 27.9% decrease in the wear rate of the composites. Possible anti-wear mechanisms are proposed based on the analyzed results of the worn surface morphology and the cross-section of the tribofilm obtained by focused ion beam transmission electron microscopy.

Keywords Plus：TRIBOLOGICAL BEHAVIORPERFORMANCECLAYPOLYESTERNANOTUBES

Published in FRICTION；10.1007/s40544-022-0720-8，MAY 2023