Abstract
With the coming era of artificial intelligence (AI) dominated by high-tech electronics, developing high-performance microwave absorption materials (MAMs) is imperative to solve the problem of increasing electromagnetic inference and pollution. Herein, a metal-organic framework (MOF)-derived CoNi bimetallic alloy (CoNi/C) with an irregular rod-like structure is prepared by a thermal reduction method. Introducing the CoNi alloy facilitates the balance between conduction loss and polarization loss and forms good impedance matching, leading to excellent microwave absorption performance. Interestingly, the optimization of absorption performance can be further achieved by controllably modulating the molar ratio of Co and Ni (Co2+/Ni2+). As expected, the obtained CoNi/C delivers excellent microwave absorption performance with a minimum reflection loss (RLmin) of -50.80 dB at 10.40 GHz and an effective absorption bandwidth (EAB) of 3.28 GHz (8.91-12.19 GHz) with a filler loading of 50 wt% at 2.0 mm. In addition, the CoNi/C can reach a maximum EAB of 4.77 GHz (12.99-17.76 GHz) at a low thickness of 1.5 mm, spanning nearly the entire Ku band. The CoNi3/C also exhibits an impressive RLmin of -44.84 dB at 3.28 GHz in the S band. This work offers a novel strategy to modulate the magnetic/electric properties of MOF-derived MAMs.
With the coming era of artificial intelligence (AI) dominated by high-tech electronics, developing high-performance microwave absorption materials (MAMs) is imperative to solve the problem of increasing electromagnetic inference and pollution.
Keywords Plus：AT-C COMPOSITES；MICROWAVE；HETEROSTRUCTURE；MICROSPHERES；CONSTRUCTION；EFFICIENT；GRAPHENE
Published in RSC ADVANCES，Volume14；10.1039/d3ra08896k，MAR 20 2024