Abstract

The iron-based high-entropy alloys are poised to become the next generation of high-temperature materials due to their outstanding mechanical properties and cost-effectiveness. In this work, the microstructure, mechanical properties, and tribological behaviors of Fe50Mn25Cr5Al15Ti5 iron-based high-entropy alloys are investigated. The grain morphology of Fe50Mn25Cr5Al15Ti5 alloy is equiaxed and dominated by BCC structure. Fe50Mn25Cr5Al15Ti5 alloy has higher hardness, better resistance to high-temperature softening and superior wear resistance than Hadfield steel (40Mn18Cr3). Within 800 degrees C, wear rate remains a low order of 10-5 mm3/N & sdot;m. At RT, abrasive wear is the dominant mechanism. At 400 degrees C, non-dense oxide layer containing unoxidized metal is formed, resulting in delamination, adhesion and abrasion. At 800 degrees C, a dense wear-resistant oxide glaze layer covers the wear surface.

Keywords Plus：MECHANICAL-PROPERTIES，BEHAVIOR，MICROSTRUCTURE，PERFORMANCE，STEEL

Published in TRIBOLOGY INTERNATIONAL，Volume 204；10.1016/j.triboint.2024.110423，APR 2025