Abstract: In this paper, three-dimensional (3D) Cu-Ce-Ox catalysts with controllable pore diameters were rationally designed and synthesized by a facile hard-template method. By controlling the calcination temperature, the 3D Cu-Ce-Ox catalysts with different pores were synthesized by nano-replication technology with KIT-6 as hard template. These catalysts expressed 3D pore structure, possessed higher pore volume and large pores, and owned more surface active sites, which were helpful for CO oxidation. When the calcination temperature of Cu-Ce-Ox was 600 degrees C, this catalyst showed the highest catalytic activity. The reason was due to its relatively stronger redox ability and surface activity species. More Ce3+, Cu+ and chemisorbed oxygen concentration was very useful in achieving the highest catalytic performance.
KeyWords Plus: CARBON-MONOXIDE OXIDATION; CUO/CEO2 CATALYSTS; MIXED OXIDES; GOLD CATALYSTS; PERFORMANCE; SUPPORT; IMPREGNATION; PRETREATMENT; REDUCTION; NANOTUBES
Published in RSC ADVANCES, 6 (69):64247-64257; 10.1039/c6ra12384h 2016