Experimental investigation on tribological behavior of several polymer materials under reciprocating sliding and fretting wear conditions

 
Abstract: This work comparatively studied the friction and wear behaviors of the six polymers (UHMWPE, PTFE, Phenolic, PHBA, PEEK and PI) under reciprocating sliding and fretting wear conditions. Hopefully, the results could contribute to provide some guidance for use and selection of materials. By investigating their friction and wear values, the morphologies of the worn surfaces and microstructures, the corresponding wear mechanisms under the two wear modes were analyzed in detail. It was also discussed the relationship between the microstructure and tribology performances of materials. The results showed that the sliding wear resistance of material was different with its fretting wear resistance. Fretting wear resistance increased orderly: PTFE < UHMWPE < PHBA < PI < PEEK < Phenolic.

KeyWords Plus: MOLECULAR-WEIGHT POLYETHYLENE; LUBRICATION CONDITIONS; CRACK INITIATION; EPOXY COMPOSITES; HIGH-TEMPERATURE; CROSS-LINKING; RESISTANCE; FRICTION; PEEK; MECHANISMS

Published in TRIBOLOGY INTERNATIONAL, 104 73-82; 10.1016/j.triboint.2016.08.030 DEC 2016

Copyright © Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences
Address: No.18,Tianshui Middle Road,Lanzhou,P.R.China ZIP Code:730000 Tel: 86-0931-4968009 Fax: 86-0931-8277088
E-mail: webeditor@licp.cas.cn Technical support: Qingyun Software